Ademix 7503 Pol Waterproof UV

Polyurethane Based UV Resistant Topcoat Coating Material

Polyurethane Based UV Resistant Topcoat Coating Material

It Is An Aliphatic Polyurethane Based, Double Component, UV Resistant, Topcoat Coating Material.

Areas of Use:
It is applied as a final coating in the protection of polyurethane waterproofing materials in roofs, terraces, verandas and balconies, stadiums and outdoor car parks, industrial floors, light roofs made of metal and fibrous materials, bridge platforms.

It is easy to apply.
It is resistant to UV rays.
It has high abrasion and chemical resistance.
Due to its aliphatic structure, it protects the color, does not discolor and turn yellow when exposed to sun rays.
It maintains its mechanical properties at temperatures between -40 ˚C and +90 ˚C.
It provides effective resistance against chemicals.
It has high adherence to the applied surface.

Technical Specifications:
Density: 1,15 ± 0,10 gr/ml
Shore A Hardness: 60
Elongation at Break: ≥ 100%
Adhesion to Concrete Strength: ≥ 2 N/mm²

Application Information:
Application Temperature: (+5°C) – (+30°C)
Mixing Ratio: 18 kg Component A / 6 kg Component B
Mixture Pot Life: 45 minutes
Ultimate Curing Time: 7 Days
Average Consumption: 0,150-0,300 kg/m²

*These values are valid for 23°C and 50% relative humidity. Times may vary depending on ambient conditions.

Surface Preparation:
-The surface must be clean and dry, and free from oil, dirt, grease, coatings and other dirt that will prevent adhesion.
-Large fractures and faults must be repaired beforehand.
-The cement crust and glossy screed sanding on the concrete surface should be cleaned with tools such as a notching machine, diamond drum wiping machine, driven grinding, and the surface should be roughened and wiped.
-The entire surface of the industrial vacuum cleaner should be cleaned from dust.
-The surface should be prepared by priming with ADEMIX 7501 POL PRIMER.

Mixture Preparation:
By adding component B on component A, ADEMIX 7503 POL WATERPROOF UV should be stirred with a 300 – 400 rev/min mixing bit drill for 2 -3 minutes until a homogeneous consistency is obtained.
The components are packed in the correct mixing ratios. If some of the product will be used, this ratio should be considered. Attention should be paid to the consumption of the prepared mixture within the pot life.

ADEMIX 7503 POL WATERPROOF is poured onto the UV primed/polyurethane, waterproofed surface and applied with a roller or brush until the entire surface is covered.
– Since the mixtures will begin to gel in 45 minutes, the pot life should be considered.

Avoid application at temperatures below -5˚C and above +30˚C.
-The surfaces to be applied should not be moist.
– It should not be applied on surfaces previously treated with silanes, siloxanes, silicones or other water-preventing agents
-All tools and application equipment should be cleaned with thinner immediately after use. Hardened/cured material can only be removed by mechanical methods.

All necessary Occupational Health and Safety measures must be taken in the application areas. All work safety equipment, such as work clothes, protective gloves/goggles /mask, should be used during the application in accordance with the Occupational Health and Safety rules. Ventilation of the working area is required. Warehouse and stock areas should not be approached with fire. Contact of the product with the skin and eyes should be prevented, in such a case, the contacted part of the skin should be washed with plenty of water and medical attention is required immediately. Food and beverages should also not come into contact with the product. It should be kept out of reach of children.


24 kg set

Component A: 18 kg tin can
Component B: 6 kg tin can

Shelf life: Storage conditions
It should be stored in its original package in a dry environment, protecting from frost.
If appropriate storage conditions are provided, it is 12 months from the production date.